For cemented carbide materials:
Storing at room temperature is fine. (Less than 300 in Celsius, as cobalt oxidizes at that temperature)
Humidity will leads to rusting, so we recommend storing the materials in an area with low humidity.
For complete metal molds:
Cemented Carbide corrosion can occur from grinding fluid, lubricating liquid, or other liquids.
If the grinding or lapping surface is not stored properly, corrosion may occur.
Store using a rust preventive oil or paper.
Q&A in the same category in this question
-
What causes cemented carbide to crack?
Compared to metal materials, cemented carbide materials have a different thermal expansion coefficient. For this reason, cracks may occur in shrink/cooling-fitted products when the operating temperature is significantly higher (lower) than the designed value. When using cemented carbides with high hardness, problems such as cracking may occur by high impact, so the required fracture toughness value should also be carefully considered.
-
What are the effects of corrosion?
We checked a cemented carbide made 20 years ago, and verified 20 microns worth of corrosion.
Only the surface was corroded, so we were able to remove it by reprocessing it.
However, there are cases where some corrosion cannot be removed due to working environments, so we recommend regrinding if the corrosion is 0.1mm or greater. If storing after regrinding, ensure that all processing liquids have been removed and dried. Apply the carbide with rust preventive oil or paper, or cover in alumina powder. -
What is the relationship between hardness and strength?
Hardness affects resistance to abrasion, and harder the material the more resistant it is to abrasion.
However, amount of abrasion is not only determined by hardness, but could be affected by adhesions caused by workpieces of certain materials.
Thickness also affects the life of material, and so the environment and manufacturing process must be taken into consideration when selecting cemented carbide grade.
There are many factors related to strength, such as transverse rupture strength, impact strength, fracture toughness value and others, therefore material selection must be made in consideration of these factors.
-
Catalog
We will provide high value-added cemented carbide with the achievements and know-how cultivated so far.
Download -
Consultation and Inquiry
We solve your problems by providing integrated solutions from material selection/development to precision machining and provision of finished products.
Contact us -
FAQ
We have posted the contents of many inquiries from customers in the past.
Click for details